EN 10216-2 Kemisk sammensætning
|
Stålkvalitet |
C |
Si |
Mn |
P |
S |
Cr |
Mo |
Ni |
Altot |
Cu |
Ti max |
|
|
Stål navn |
Stål nummer |
max |
max |
|||||||||
|
P195GH |
1.0348 |
=0.13 |
=0.35 |
=0.70 |
0.025 |
0.020 |
=0.30 |
=0.08 |
=0.30 |
=0.020 |
=0.30 |
0.040 |
|
P235GH |
1.0345 |
=0.16 |
=0.35 |
=1.20 |
0.025 |
0.020 |
=0.30 |
=0.08 |
=0.30 |
=0.020 |
=0.30 |
0.040 |
|
P265GH |
1.0425 |
=0.20 |
=0.40 |
=1.40 |
0.025 |
0.020 |
=0.30 |
=0.08 |
=0.30 |
=0.020 |
=0.30 |
0.040 |
|
16 Mo3 |
1.5415 |
0.12-0.20 |
0.40-0.90 |
0.40-0.90 |
0.025 |
0.020 |
=0.30 |
0.25-0.35 |
=0.30 |
=0.040 |
=0.30 |
|
|
14MoV6-3 |
1.7715 |
0.10-0.15 |
0.15-0.35 |
0.40-0.70 |
0.025 |
0.020 |
0.30-0.60 |
0.40-0.50 |
=0.30 |
=0.040 |
=0.30 |
|
|
13CrMo4-5 |
1.7335 |
0.10-0.17 |
=0.15 |
0.40-0.70 |
0.025 |
0.020 |
0.70-1.15 |
0.40-0.60 |
=0.30 |
=0.040 |
=0.30 |
|
|
10CrMo9-10 |
1.7380 |
0.08-0.14 |
0.08-0.14 |
0.30-0.70 |
0.025 |
0.020 |
2.00-2.50 |
0.90-1.10 |
=0.30 |
=0.040 |
=0.30 |
|
|
25CrMo4 |
1.7218 |
0.22-0.29 |
0.22-0.29 |
0.60-0.90 |
0.025 |
0.020 |
0.90-1.20 |
0.15-0.30 |
=0.30 |
=0.040 |
=0.30 |
|
|
15NiCuMoNb5-6-4 |
1.6368 |
=0.17 |
=0.17 |
0.80-1.20 |
0.025 |
0.020 |
=0.30 |
0.25-0.50 |
1.00-1.30 |
=0.050 |
0.50-0.80 |
|
|
X10CrMoVNb9-1 |
1.4903 |
0.08-0.12 |
0.08-0.12 |
0.30-0.60 |
0.025 |
0.020 |
8.00-9.50 |
0.85-1.05 |
=0.40 |
=0.040 |
=0.30 |
|
|
a Elementer, der ikke er medtaget i denne tabel, må ikke med vilje tilføjes stålet uden købers samtykke, bortset fra elementer, som kan tilføjes til færdiggørelse af støbningen. Alle passende foranstaltninger skal træffes for at forhindre tilsætning af uønskede elementer fra skrot eller andre materialer, der anvendes i stålfremstillingsprocessen |
||||||||||||
|
b Dette krav gælder ikke, forudsat at stålet indeholder en tilstrækkelig mængde andre nitrogenbindende elementer, som skal rapporteres. Ved brug af titanium skal producenten verificere, at (Al+Ti/2)=0,020 % |
||||||||||||
|
c Mulighed 2: For at lette efterfølgende formningsoperationer gælder et aftalt maksimalt kobberindhold, der er lavere end angivet, og et aftalt specificeret maksimalt tinindhold |
||||||||||||
|
d Indholdet af disse elementer skal ikke rapporteres, medmindre det med vilje er tilføjet rollebesætningen |
||||||||||||
|
e For vægtykkelse=30 mm kan kulstofindholdet øges med 0,02 % til støbning og produktanalyse |
||||||||||||
|
f Den øvre kulstofværdi på 0,23 % må ikke overskrides ved produktanalyse |
||||||||||||
EN 10216-2 Mekanisk egenskab
|
Stålkvalitet |
Trækegenskaber ved stuetemperatur |
Effektegenskaber ab |
|||||||||||
|
Stål navn |
Stål nummer |
Øvre flydespænding eller prøvestyrke ReH eller Rp0,2 for vægtykkelse T Min. |
Trækstyrke Styrke Rm |
Forlængelse Et min. % a |
Minimum gennemsnitlig absorberet energi KV J ved en temperatur på grader |
||||||||
|
T Mindre end eller lig med 16 |
160 |
40 |
60 |
l |
t |
l |
t |
||||||
|
MPa |
MPa |
MPa |
MPa |
MPa |
20 |
0 |
-10 |
20 |
0 |
||||
|
P195GH |
1.0348 |
195 |
320-440 |
27 |
25 |
40 c |
28 d |
27c |
|||||
|
P235GH |
1.0345 |
235 |
225 |
215 |
360-500 |
25 |
23 |
40 c |
28 d |
27c |
|||
|
P265GH |
1.0425 |
265 |
255 |
245 |
410-570 |
23 |
21 |
40 c |
2s d |
27C |
|||
|
16 Mo3 |
1.5415 |
280 |
270 |
260 |
450-600 |
22 |
20 |
40 c |
27 c |
||||
|
14MoV6-3 |
1.7715 |
320 |
320 |
310 |
460-610 |
20 |
18 |
40 c f |
27 c |
||||
|
13CrMo4-5 |
1.7335 |
290 |
290 |
280 |
440-590 |
22 |
20 |
40 c |
27 c |
||||
|
10CrMo9-10 |
1.7380 |
280 |
280 |
270 |
480-630 |
22 |
20 |
40 c |
27 c |
||||
|
25CrMo4 |
1.7218 |
345 |
345 |
345 |
540-690 |
18 |
15 |
40 c f |
27 c |
||||
|
15NiCuMoNb5-6-4 |
1.6368 |
440 |
440 |
440 |
440e |
610-780 |
19 |
17 |
40 c f |
27 c |
|||
|
X10CrMoVNb9-1 |
1.4903 |
450 |
450 |
450 |
450 |
630-830 |
19 |
17 |
40 c f |
27 c |
|||
|
a I=langsgående t=tværgående |
|||||||||||||
|
b Skal verificeres, når valgmulighed 4 og/eller 5 er specificeret, medmindre fodnote f) gælder |
|||||||||||||
|
c Mulighed 4: Effektenergi skal verificeres. |
|||||||||||||
|
d Mulighed 5: Den langsgående anslagsenergi skal verificeres. |
|||||||||||||
|
e Til vægtykkelse 60 mm< T =80mm |
|||||||||||||
|
f Slagprøve obligatorisk for vægtykkelse T =16mm |
|||||||||||||
EN 10216-2 kedelrør Varmebehandling
|
Stålkvalitet |
Varmebehandling a |
Austeniserende |
Temperering |
|||
|
Stål navn |
Stål nummer |
Temperatur grad |
Kølende medium |
Temperatur grad |
Kølemedium |
|
|
P195GH |
1.0348 |
+N b |
880 til 940 |
Luft |
- |
- |
|
P235GH |
1.0345 |
+N b |
880 til 940 |
Luft |
- |
- |
|
P265GH |
1.0425 |
+N b |
880 til 940 |
Luft |
- |
- |
|
16 Mo3 |
1.5415 |
+N b |
890 til 950 |
Luft |
- |
- |
|
14MoV6-3 |
1.7715 |
+NT bc |
930 til 990 |
Luft |
680 til 730 |
luft |
|
13CrMo4-5 |
1.7335 |
+NT bc |
900 til 960 |
Luft |
660 til 730 |
luft |
|
10CrMo9-10 |
1.738 |
+NT bc |
900 til 960 |
Luft |
680 til 750 |
luft |
|
25CrMo4 |
1.7218 |
+QT |
860 til 900 |
Luft eller væske |
620 til 680 |
luft |
|
15NiCuMoNb5-6-4 |
1.6368 |
+NT c |
880 til 980 |
Luft |
580 til 680 |
luft |
|
X10CrMoVNb9-1 |
1.4903 |
+NT c |
1040 til 1090 |
luft |
730 til 780 |
luft |
|
a +N=Normalisering, +NT=Normalisering + Tempering, +QT=Slukning + Tempering (luft eller væske), +I=Isotermisk udglødning. |
||||||
|
b Normalisering omfatter normalisering af formning. |
||||||
|
c For these steel grades it may be necessary in the case of wall thickness T above 25 mm or T/D >0,15 for at anvende bratkøling og temperering for at opnå den tilsigtede struktur og materialeegenskaber. Beslutningen skal overlades til producentens skøn, men skal meddeles kunden på tidspunktet for forespørgsel og bestilling. Stålrør, der er behandlet på en sådan måde, skal betegnes med stålnavnet suppleret med symbolet +QT. |
||||||